DeepDyve requires Javascript to function. Please enable Javascript on your browser to continue.
Low-Cost High Performance Polyamide Thin Film Composite (Cellulose Triacetate/Graphene Oxide) Membranes for Forward Osmosis Desalination from Palm Fronds
Low-Cost High Performance Polyamide Thin Film Composite (Cellulose Triacetate/Graphene Oxide)...
Jamil, Tarek S.;Nasr, Rabab A.;Abbas, Hussien A.;Ragab, Tamer I. M.;Xabela, Sinethemba;Moutloali, Richard
2021-12-22 00:00:00
membranes Article Low-Cost High Performance Polyamide Thin Film Composite (Cellulose Triacetate/Graphene Oxide) Membranes for Forward Osmosis Desalination from Palm Fronds 1 1 , 2 3 4 Tarek S. Jamil , Rabab A. Nasr *, Hussien A. Abbas , Tamer I. M. Ragab , Sinethemba Xabela and Richard Moutloali National Research Center El Behouth Street Dokki, Water Pollution Control Department, Dokki 12622, Cairo, Egypt; omaytarek73@yahoo.com National Research Centre, Inorganic Chemistry Department, El Behouth Street Dokki, Dokki 12622, Cairo, Egypt; hu_abbas2005@yahoo.com National Research Centre, Chemistry of Natural and Microbial Products Department, Dokki 12622, Cairo, Egypt; tamerragab2006@gmail.com Department of Chemical Sciences, University of Johannesburg, Doornforntein 2028, South Africa; sinethembaxabela@gmail.com Campus Florida, Institute for Nanotechnology and Water Sustainability, College of Science, Engineering and Technology, Florida Science, University of South Africa, Johannesburg 1709, South Africa; moutlrm@unisa.ac.za * Correspondence: rababelsheikh@yahoo.com Abstract: Novel low-cost cellulose triacetate-based membranes extracted from palm fronds have been fabricated through the phase–inversion procedure. The cellulose tri-acetate (CTA) membrane was modified by incorporation of graphene oxide (GO) prepared from palm fronds according Citation: Jamil, T.S.; Nasr, R.A.; to the modified Hummer method as well as the preparation of polyamide thin film composite Abbas, H.A.; Ragab, T.I.M.; Xabela, S.; CTA membranes to improve forward osmosis performance for seawater desalination. The surface Mutloali, R. Low-Cost High characteristics and morphology of the prepared CTA, GO, and the fabricated membranes were Performance Polyamide Thin Film investigated. The modified TFC prepared membrane had superior mechanical characteristics as well Composite (Cellulose as permeation of water. The performance of the prepared membranes was tested using synthetic Triacetate/Graphene Oxide) 2 M Sodium chloride (NaCl) feed solution. The water flux (J ) of the thin-film composite (TFC) Membranes for Forward Osmosis (CTA/0.3% GO) was 35 L/m h, which is much higher than those of pure CTA and CTA/0.3% GO. Desalination from Palm Fronds. Membranes 2022, 12, 6. https:// Meanwhile, the salt reverse flux TFC (CTA/0.3% GO) was 1.1 g/m h), which is much lower than doi.org/10.3390/membranes12010006 those of pure CTA and CTA/0.3%. GO (Specific salt flux of TFC (CTA/0.3% GO) substrate membrane was 0.03 g/L indicating good water permeation and low reverse salt flux of the TFC membrane Academic Editor: Jega Veeriah compared to CTA. A real saline water sample collected from Hurgada, Egypt, with totally dissolved Jegatheesan solids of 42,643 mg/L with NaCl as the draw solution (DS) at 25 C and flow rate 1.55 L/min, was Received: 21 November 2021 used to demonstrate the high performance of the prepared TFC membrane. The chemical analysis of Accepted: 9 December 2021 desalted permeated water sample revealed the high performance of the prepared TFC membrane. Published: 22 December 2021 Consequently, the prepared low-cost forward osmosis (FO) thin-film composite CTA membranes can Publisher’s Note: MDPI stays neutral be introduced in the desalination industry to overcome the high cost of reverse osmosis membrane with regard to jurisdictional claims in usage in water desalination. published maps and institutional affil- iations. Keywords: cellulose triacetate; palm fronds; forward osmosis; thin-film composite membranes; graphene oxide Copyright: © 2021 by the authors. Licensee MDPI, Basel, Switzerland. 1. Introduction This article is an open access article The crisis of global water demands necessitates innovative and novel technologies that distributed under the terms and provide not only elevated throughput and productivity but also enclose optimum energy conditions of the Creative Commons efficiency. Today, the most compatible and effective technology to produce fresh water from Attribution (CC BY) license (https:// seawater is desalination using the reverse osmosis (RO) process. However, the high energy creativecommons.org/licenses/by/ consumption and membrane fouling are the main challenges for large-scale application. 4.0/). Membranes 2022, 12, 6. https://doi.org/10.3390/membranes12010006 https://www.mdpi.com/journal/membranes Membranes 2022, 12, 6 2 of 24 The spontaneous seepage of a solvent across a semipermeable barrier is referred to as forward osmosis (FO) [1,2]. Thermodynamically, FO process itself is spontaneous and requires no energy (if disregarding the energy for circulation) [3]. In general, during forward osmosis desalination processes, water flows from the feed solution (FS) to the draw solution (DS) where the feed solution becomes concentrated and the DS becomes diluted [4]; then product water is then separated from the diluted draw solution in the simple thermal distillation column recovery system for bench scale FO unit, but in hydride FO plant, the DS recovery system may be thermal distillation or RO unit according to the type of DS and the capacity of the FO plant. As a result, when FO is combined with a renewable energy DS recovery system, such energies would only be used for solute recovery, as FO benefits from being largely unpressurised, resulting in significant energy savings for FO desalination systems when compared to mainstream technologies such as RO [5]. FO processes have demonstrated benefits in terms of low fouling potential, ease of cleaning, bearing to high salinity, making them suitable for the treatment of high total dissolved solids (TDS) feed streams, and high-fouling load, such like landfill leachate, pharmaceutical, oil and gas produced water [6,7]. Cellulose acetate (CA) as well as cellulose triacetate (CTA) are the most widely utilized commercial membranes for FO applications. Due to its permeability and high hydrophilic- ity, CTA can be utilized in FO membrane fabrication. On the contrary, intensive reverse solute flux may hinder its extensive usage. Accordingly, the development of CTA-based FO membranes can be attained through the reduction of reverse solute flow [6]. Many articles have been reported on the preparation and performance of FO membranes such as cellulose acetate (CA) FO flat-sheet membranes [8], and the hollow fiber type of the CA membrane [9] revealed an extremely high solute reverse flux. To improve the performance of the FO membrane, various additives such as lactic acid, malic acid, and zinc chloride have been used as pore-forming agents [10]. Several hydrophilic nano-fillers, including aluminum oxide (Al O ), carbon nanotubes (CNTs), silica (SiO ), zeolite, zinc oxide (ZnO), 2 3 2 have been used to improve the performance of membranes in recent decades [11]. Because of its mechanical and electrical properties, GO has recently received significant attention in membrane enhancement. Because of the many reactive groups (e.g., OH, COOH) that enhance covalent or ionic interactions between the GO and the polymer matrix [12]. More recently, attention has been directed toward thin-film composite FO membranes due to the superior efficiency and broad pH implemented range. TFC-FO membranes are composed of two layers: an ultrathin layer above a porous substrate due to their high mechanical strength, satisfactory salt rejection, and hydrolytic stability [13,14]. Recently, phase inver- sion (a controlled polymer transformation technique from a liquid to solid phase) [15], interfacial polymerization (backed to two or more monomers that grow as polymer at the surface between two immiscible phases) [16,17], and layer-by-layer deposition (the film formation by deposition of oppositely charged layers) [17] strategies have been used to fabricate TFC–FO membranes. The objective of this study is the preparation of low cost and energy-saving FO membranes for water desalination by modification of CTA by GO where both CTA and GO were prepared from palm fronds agro-waste that considered a renewable and abundant agricultural waste in Egypt, making it a potentially low-cost source of cellulose CTA-GO membrane was prepared via the incorporation of graphene oxide in membranes. TFC polyamide/CTA-GO was prepared via the interfacial polymerization method to improve the morphology, hydrophilicity, and FO efficiency as well as antifouling, consequently, enhancing the FO performance. To verify the high performance of the TFC-CTA modified membrane for desalination of saline water, a real feed water sample has been collected from Hurgada–Red Sea coast of Egypt with salinity 42,643 mg/L with NaCl as the draw solution (DS) at ambient temperature and a flow rate 1.55 L/min Membranes 2022, 12, 6 3 of 24 2. Experimental 2.1. Materials Toluene, ethanol, sodium hydroxide, sodium hypochlorite, potassium hydroxide, methylene chloride, glacial acetic acid, H SO , chloroform, NaNO , H PO , KMnO H O , 2 4 3 3 4 4, 2 2 HCl, and Dimethylformamide (DMF) were delivered via Sigma Aldrich. For the interfacial polymerization (IP) procedure, very high purity (>99%) of m-phenylenediamine, trimesoyl chloride, and n-hexane were utilized, and >99.5% NaCl as draw solute was used. 2.2. Preparation of Cellulose Triacetate from Palm Fronds Palm frond wastes were obtained from the Siwa oasis, dried, milled into powder and dewaxed in a mixture of toluene and ethanol overnight, and the crude cellulose was extracted by using sodium hydroxide. The crude cellulose was bleached using sodium hypochlorite. The bleached cellulose was treated with potassium hydroxide to extract -Cellulose, and lastly, acetylation of cellulose was conducted by dissolving in methy- lene chloride, acetic anhydride, glacial acetic acid, H SO in accordance with our prior 2 4 work [18,19]. 2.3. Synthesis of Graphene Oxide (GO) GO was prepared from palm fronds according to the modified Hummer method [20]. Palm fronds wastes were heated at 650 C. 5 g from prepared graphite and 2.5 g NaNO was mixed with 108 mL H SO and 12 mL H PO in an ice bath for 10 min. Then, 15 g 2 4 3 4 of KMnO was added gradually while keeping the temperature of the mixture below 5 C. The suspension was stirred for 60 min in an ice bath after reacting for 2 h in an ice bath. It was then stirred for another 60 min in a 40 C water bath. The temperature of the mixture was kept constant at 98 C for 60 min while the water was continuously added. Deionized water was then added until the suspension had a volume of 400 mL. After 5 min, 15 mL of H O was added. The reaction product was centrifuged and washed repeatedly 2 2 with deionized water and a 5% HCl solution. Finally, the graphene oxide was dried at a temperature of 60 C. 2.4. CTA Fabricated Membrane A phase inversion technique was introduced for FO fabrication. Dried CTA prepared from palm fronds was added to a container containing dimethylformamide (DMF) using weight ratio20 polymer: 80 solvent weight ratio and was stirred using a mechanical stirrer. Preceding to the membrane casting, the casting glass sheet was cleaned with tap water and acetone then dried before use. The mixture was stirred at 30 C until a homogeneous solution was obtained. To eliminate air bubbles, the polymer mixture was placed at 30 C in the oven for an hour. The polymer solution was cast onto a dry-clean glass sheet using 200m casting knife. After 45 s for partial solvent evaporation, the glass sheet was immersed into a water coagulation bath at 20 C. The as-cast membrane was detached from the glass plate and submerged in a tap water bath. CTA membranes were annealed in a hot DI water bath at 75 C for 2 min. 24 h drenching in deionized water is introduced to the solidified membranes before the performance test [21]. 2.5. CTA/GO Membrane Preparation GO was introduced to DMF solvent and then ultra-sonication for 30 min before dis- solving CTA in the blended solution. The mixture was stirred at 30 C until a homogeneous solution was obtained. Then the solution was kept in an oven at 30 C for several hours to tear out the air bubbles. The compartments of the cast solution, according to the previously reported [21,22], are listed in Table 1. Membranes 2022, 12, 6 4 of 24 Table 1. The compositions of the casting solution. Polymer% Solvent% CTA (wt %) DMF %(wt %) GO% (wt %) M1 20 80 0 M2 19.9 80 0.1 M3 19.7 80 0.3 M4 19.5 80 0.5 Membrane performance can be influenced by three major parameters: polymer com- position, solvent type in the polymer solution mixture, and demixing rate during the coagulation bath. The type of demixing that occurs during phase inversion (PI) using DMF, which has been reported to be quick, results in drop-shaped voids. DMF has a high polymer solubility parameter. The DMF-based casting mixture precipitates in a very short period of time [23]. The coagulation bath temperature, on the other hand, is an important factor in de- termining membrane properties that impacts the phase inversion thermodynamics and membrane structure. The bath temperature affects the rate of the solvent–non-solvent exchange and the movement of the polymer chains. Thermodynamically, a higher tempera- ture results in faster movement of the polymer chains, improving the rearrangement of the polymer chain at the skin layer before the CTA chains are fixed by solidification. Presently, the cast film was immersed in water at 20 C since higher bath temperatures are reported to lower water permeability of the resultant membranes [21]. 2.6. Preparation of Polyamide Thin Film Composite on CTA/GO Support The interfacial polymerization (IP) technique was used for the preparation of the polyamide (PA) active layer on a CTA/0.3%GO substrate using MPD and TMC monomers. First, hydrolysis of the cellulose triacetate membranes in NaOH solution (0.7 wt%, 30 min) was undertaken, fabricating more permeable membranes for both water and salt [24].The substrate was sunken in a 2.0 wt% MDP aqueous solution for a minute then the extra used MPD solution was taken away, then, 0.1 wt% TMC solution in n-hexane was introduced to the above-soaked substrate for 1 min. To remove the residual monomers TFC membrane was rinsed with DI water [25]. 2.7. The Fabricated Membrane’s Performance The efficiency of the fabricated membrane was examined through an in-house de- signed FO lab-scale unit (Figure 1), where DI water was used as the feed solution and 2 M NaCl was used as the draw solution. The product water was then separated from the diluted draw solution in the simple thermal distillation column recovery system. The permeation properties of the prepared membranes were evaluated using a cross- flow filtration unit at a trans-membrane pressure (TMP) of 1.55 MPa and 1 L/min feed flow rate. The water flux (Jw) (Equation (1)) of the membrane was gained by calculating the water ’s volume (DV) passing through the active and efficient filtration area (Am) of the membrane through the collection time of the sample (D t), the effective filtration area of all the membranes was 56.3 cm . DV Jw = (1) D t Am A (water permeability) was calculated by Jw A = . (2) D P Membranes 2022, 12, 6 5 of 24 Membranes 2021, 11, x FOR PEER REVIEW 5 of 25 The salt permeability coefficient (B) was calculated at 1.55 MPa and 2 M NaCl solution by Equation (3); 1 1 B = Jw B 1 = Jw(( ) − 1) (3) (3) The apparent salt rejection (R) was calculated using Equation (4) The apparent salt rejection (R) was calculated using Equation (4) CNaCl,ds ×Vds CNaCl, R% = ds (1 − Vds ) × 100. (4) Cfs0×Vfs0 R% = 1 100. (4) Cfs0 Vfs0 Using pure DI H2O as an FS, the reverse DS flux was estimated by Equation (5) Using pure DI H O as an FS, the reverse DS flux was estimated by Equation (5) 𝐶 𝑉 −𝐶 𝑉 𝑓 𝑓 0 0 Js = (5) AΔt C V C V f f 0 0 Js = (5) where Js is the reverse salt flux (g/m · h), C0 is the initial feed concentration expressed in ADt g/L and Cf refers to the final feed concentration (g/L), V0 and Vf refers to the initial and where Js is the reverse salt flux (g/m h), C is the initial feed concentration expressed in final volumes of the feed solution (L), respectively, Δt is the time (h), and A is the active g/L and C refers to the final feed concentration (g/L), V and V refers to the initial and fand efficient filtration area membrane surface 0 area (mf ) [26]. final volumes of the feed solution (L), respectively, Dt is the time (h), and A is the active and efficient filtration area membrane surface area (m ) [26]. Figure 1. The schematic diagram for bench scale forward osmosis (FO) unit. Figure 1. The schematic diagram for bench scale forward osmosis (FO) unit. 2.8. Characterization of Prepared Materials 2.8. Characterization of Prepared Materials The prepared CTA and GO were fully characterized by XRD measurements using (D8 The prepared CTA and GO were fully characterized by XRD measurements using Advance, Bruker, Germany) diffractometer equipped with a position-sensitive detector Lynxeye (Cu (D8 K A= dv1.54 anceÅ). , Bruke FTIR r, G (6100 ermaJasco., ny) diff T ra okyo, ctomJapan) eter equ Spectr ippedum with equipment a position- with sensitive detec- 1 1 −1 4 cm resolution tor Lynx and eyefr (Cu equency Kα = 1range .54 Å).of FTIR 400–4000 (6100 cm Jasco.,was Japa utilized n) Spectr for um recor equi ding pmen the t with 4 cm −1 FTIR spectra of samples. An SEM (S3400N, Hitachi, Japan) was utilized to determine resolution and frequency range of 400–4000 cm was utilized for recording the FTIR spec- the morphology tra of s of am samples. ples. AnNuclear SEM (S3magnetic 400N, Hita resonance chi, Japan (NMR) ) was uti was lized determined to determi using ne the morphol- an Avance III 400 MHz Bruker High-performance digital, FT-NMR spectrometer. The ogy of samples. Nuclear magnetic resonance (NMR) was determined using an Avance III prepared membranes were also fully characterized by FT-IR, porosity, the water contact 400 MHz Bruker High-performance digital, FT-NMR spectrometer. The prepared mem- angle measurement as well as morphological and mechanical properties of the prepared branes were also fully characterized by FT-IR, porosity, the water contact angle measure- membranes. A tensile test was performed using the H5KS universal tensile measuring ment as well as morphological and mechanical properties of the prepared membranes. A unit in which the space between the handles was set to 200 mm and the thickness of the tensile test was performed using the H5KS universal tensile measuring unit in which the membranes measured was 25 mm. Samples were stretched at a steady elongation rate of space between the handles was set to 200 mm and the thickness of the membranes meas- 30 mm/min using a collection of five samples to obtain the average reading. ured was 25 mm. Samples were stretched at a steady elongation rate of 30 mm/min using a collection of five samples to obtain the average reading. 3. Results and Discussions 3.1. Material’s Characterization 3. Results and Discussions 3.1.1. Characterization of CTA 3.1. Material’s Characterization Figure 2a shows the XRD pattern of cellulose triacetate. The peaks detected at 12.27, 3.1.1. Characterization of CTA 15.8, 20.6, and 33.7 were characteristic of I phases of cellulose [27–30]. The peak detected at Figure 2a shows the XRD pattern of cellulose triacetate. The peaks detected at 12.27, 8.7 was characteristic of the semicrystalline acetylated derivative cellulose. The substitution 15.8, 20.6, and 33.7 were characteristic of Iβ phases of cellulose [27–30]. The peak detected of a hydroxyl group by the acetyl groups breaks the inter and intramolecular hydrogen at 8.7 was characteristic of the semicrystalline acetylated derivative cellulose. The substi- bond of cellulose which lead to a decrease in the degree of the crystallinity [31]. tution of a hydroxyl group by the acetyl groups breaks the inter and intramolecular hy- drogen bond of cellulose which lead to a decrease in the degree of the crystallinity [31]. Membranes 2021, 11, x FOR PEER REVIEW 6 of 25 Membranes 2022, 12, 6 6 of 24 CTA 20 40 60 2q T % 4000 3600 3200 2800 2400 2000 1600 1200 800 400 -1 Wavenumber cm Figure 2. (a) XRD and (b) FTIR spectrum for cellulose (triacetate) prepared from palm fronds. Figure 2. (a) XRD and (b) FTIR spectrum for cellulose (triacetate) prepared from palm fronds. −1 1 Figure 2b shows the FTIR spectrum for cellulose triacetate. The peak at 1730 cm was Figure 2b shows the FTIR spectrum for cellulose triacetate. The peak at 1730 cm −1 1 characteristic to wide CO band for bonding acetyl groups. A small band at 1369 cm was was characteristic to wide CO band for bonding acetyl groups. A small band at 1369 cm −1 1 assigned to C–H bond in OCOCH3 group and the band detected at 1240 cm was assigned was assigned to C–H bond in OCOCH group and the band detected at 1240 cm was −1 1 to CO stretching of acetyl groups [32]. An intensive band at 1051 cm was assigned to assigned to CO stretching of acetyl groups [32]. An intensive band at 1051 cm was assigned skeletal v to ibskeletal ration fro vibration m the C fr O om C pyra the C no O se Cri pyranose ng. There ring. are n Ther o bae nd ar s ed no etebands cted fo detected r the un- reacted acetic anhydride and the by-product, acetic acid [33]. The peaks at 1050 and 1390 for the unreacted acetic anhydride and the by-product, acetic acid [33]. The peaks at 1050 −1 and cm 1390 backed cm tobacked C–O alto coC–O holic alcoholic stretch an str detch C–H and from C–H cell fr ulo om se cea llulose nd hemi and cell hemicelluloses, uloses, respec- rti espectively vely [34]. [34]. NMR NMRspectr spectro oscopy scopy is is an anelucidation elucidationtool toolfor for CT CT A Astr stuctur ructure e definition. definition.NMR NMRpr pr oves oves the formation of CTA through acetylating CA. Figure 3a shows the proton NMR as an the formation of CTA through acetylating CA. Figure 3a shows the proton NMR as an indicator for the degree of substitution (DS). The ratio of the seven anhydrocellulose proton indicator for the degree of substitution (DS). The ratio of the seven anhydrocellulose pro- absorbance was utilized in the specific range between 3.6 mg/L and 5.1 mg/L to the ton absorbance was utilized in the specific range between 3.6 mg/L and 5.1 mg/L to the absorbance of three methylated protons of acetyl group between 1.8 mg/L and 2.1 mg/L. absorbance of three methylated protons of acetyl group between 1.8 mg/L and 2.1 mg/L. DS resulted from dividing 1/3 (acetyl peak area) by 1/7 (anhydroglucose area). DS Acetyl DS resulted from dividing 1/3 (acetyl peak area) by 1/7 (anhydroglucose area). DS Acetyl resulted from the ratio of spectral integrals of acetyl moiety to the repeating unit. The DS resulted from the ratio of spectral integrals of acetyl moiety to the repeating unit. The DS of crude cellulose acetate was 2.83 and soluble chloroform3.17. Accordingly, it was proven of crude cellulose acetate was 2.83 and soluble chloroform3.17. Accordingly, it was proven that the average DS was nearly the same at the individual 2, 3, and 6 hydroxyl positions of that the average DS was nearly the same at the individual 2, 3, and 6 hydroxyl positions the glycosyl ring (DS , DS , and DS ). 2 3 6 of the glycosyl ring (DS2, DS3, and DS6). Intensity Membranes 2021, 11, x FOR PEER REVIEW 7 of 25 C-NMR showed significant signals appearing at δ value170.7 referring to carbonyl carbon plus that at δ value20.5, δ20.6, 21.0, and δ21.5 set for methyl carbons, which was not detected in the cellulose spectrum confirming the supposed form of acetyl cellulose structure, as shown in Figure 3b. In addition, carbons attached to the acetyl groups became slightly shifted down field than the parent structure. In addition, the amount of substi- tuted carbon was identified by C spectrum. Chloroform soluble cellulose acetate spec- trum indicated the highest number of carbons, i.e., C spectrum of chloroform soluble cel- Membranes 2022, 12, 6 7 of 24 lulose acetate revealed the presence of 24 carbons. Membranes 2021, 11, x FOR PEER REVIEW 8 of 25 1 13 1 13 Figure 3. (a) H NMR spectrum of chloroform soluble CA palm fronds (b) C NMR spectrum of chloroform soluble CA Figure 3. (a) H NMR spectrum of chloroform soluble CA palm fronds (b) C NMR spectrum of palm fronds. chloroform soluble CA palm fronds. 3.1.2. Characterization of Graphene Oxide Graphene oxide was obtained from palm fronds through graphite by hammer tech- nique [35]. Figure 4a showed the XRD pattern of graphene oxide. The diffraction peak at 2 θ = 12.68°correspondedto graphene oxide [35], which was in agreement with that de- tected at 2 θ = 11.6° for graphene oxide prepared from agricultural sugarcane bagasse oxidation [36]. Decreasing the intensity of the native graphite peak, between 2 θ of 25° and 30°, revealed the oxidation of the starting graphite to graphene oxide [37]. Membranes 2022, 12, 6 8 of 24 C-NMR showed significant signals appearing at value170.7 referring to carbonyl carbon plus that at value20.5, 20.6, 21.0, and 21.5 set for methyl carbons, which was not detected in the cellulose spectrum confirming the supposed form of acetyl cellulose structure, as shown in Figure 3b. In addition, carbons attached to the acetyl groups became slightly shifted down field than the parent structure. In addition, the amount of substituted carbon was identified by C spectrum. Chloroform soluble cellulose acetate spectrum indicated the highest number of carbons, i.e., C spectrum of chloroform soluble cellulose acetate revealed the presence of 24 carbons. 3.1.2. Characterization of Graphene Oxide Graphene oxide was obtained from palm fronds through graphite by hammer tech- nique [35]. Figure 4a showed the XRD pattern of graphene oxide. The diffraction peak at 2 = 12.68 correspondedto graphene oxide [35], which was in agreement with that Membranes 2021, 11, x FOR PEER REVIEW 9 of 25 detected at 2 = 11.6 for graphene oxide prepared from agricultural sugarcane bagasse oxidation [36]. Decreasing the intensity of the native graphite peak, between 2 of 25 and 30 , revealed the oxidation of the starting graphite to graphene oxide [37]. graphene oxide 4000 3500 3000 2500 2000 1500 1000 500 -1 Wave number (cm ) Figure 4. (a) XRD patterns of graphite and graphene oxide. The inset shows the characteristic Figure 4. (a) XRD patterns of graphite and graphene oxide. The inset shows the characteristic gra- phene oxide extension peak and (b) FT-IR spectrum of graphene oxide. graphene oxide extension peak and (b) FT-IR spectrum of graphene oxide. −1 The band at 3000–3650 cm in Figure 4b was attributed to the extended pulses of OH −1 groups of H2O molecules adsorbed on GO. The peak of 1623 cm was assigned to the −1 stretching vibration of C=C, while the peak of 700 cm stretching vibration of C=O of car- boxylic acid and carbonyl groups presented at the boundaries of graphene oxide. The −1 peak of 1390 cm was attributed to the extended pulses of C–O of carboxylic acid. Mean- −1 while, the peak of 1063 cm was attributed to the extended pulses C–OH of alcohol [35]. Transmittance (%) Membranes 2022, 12, 6 9 of 24 The band at 3000–3650 cm in Figure 4b was attributed to the extended pulses of OH groups of H O molecules adsorbed on GO. The peak of 1623 cm was assigned to the stretching vibration of C=C, while the peak of 700 cm stretching vibration of C=O of carboxylic acid and carbonyl groups presented at the boundaries of graphene oxide. The peak of 1390 cm was attributed to the extended pulses of C–O of carboxylic acid. Meanwhile, the peak of 1063 cm was attributed to the extended pulses C–OH of alcohol [35]. 3.1.3. Characterization of Prepared CTA and CTA/GO Membrane Contact Angle Prepared CTA and CTA/GO Membrane The contact angle values show that the CTA/GO membranes become more hydrophilic as GO- was incorporated into the cellulose triacetate membrane matrix. The water con- tact angle diminished from 65 (pure CTA membrane) to 47 as the amount of GO was increased to 0.3 wt% GO. The water-loving membrane could drop off the immediate interplay between the adsorbed thin layer of water molecules on the top of the mem- brane [38]. The GO enhanced the membrane’s surface negativity due to the existence of oxygen-containing functional groups such as hydroxyl, epoxy groups, and carboxyl groups in GO which increase the interaction of membrane and water molecules, resulting in increased hydrophilicity. A significant decrease in contact angle after the addition of 0.3 wt% GO content was observed, demonstrating a significant increase of surface hydrophilicity which is envisaged to confer greater FO flux performance. This is supposed to be related to hydrophilic GO movement toward the top layer during phase inversion, leading to the lower water contact angles because of the GO’s superior attraction of OH groups, however, the contact angle of 0.5 wt% GO was 54. This might be attributed to the bad dispersion of GO onto the surface of the membrane surface, as well as the bad compatibility and adhesive forces between the GO and the polymer, as the filler content was increased. SEM Prepared CTA and CTA/GO Membrane The morphological structures of the CTA and CTA-GO (0.1, 0.3, and 0.5 wt%) mem- branes were evaluated through SEM (Figure 5). Pure CTA membranes showed the existence of both sponge and a few macrovoid structures in the cross-section area, which is distin- guishing of corresponding membranes [39,40]. The increase of these macrovoid structures on the addition of GO to CTA-GO membranes seems to be larger in comparison to pure CTA membranes (Figure 5). CTA-GO membranes are endowed with an appreciable pore size compared to that of pure CTA membranes, which give rise to high water permeability. The surface of the CA membrane, after the adding of GO, shows well distribution of GO particles onto the polymer matrix. Moreover, no cracks were observed on the membrane’s surface on the addition of GO indicating the GO membrane’s strength. From the SEM analysis, the cross-section area decreased in thickness after the addition of 0.1 wt% GO and could be due to hydrophilic GO particles, which can increase the rate of water (non-solvent) and solvent mixing during phase inversion, leading to a relatively lean top surface [41]. The thickness descends due to the incorporation of GO, which is aligned with previous studies [42]. Furthermore, an increase in the number of GO particles augmented the viscosity of the dope solution leading to a diminished mass transfer rate of the non-solvent, giving rise to the thickness of the skin layer. When the quantity of GO on the CTA matrix was raised to 0.5 wt%, macrovoids reduced and the connectivity of the holes was subdued, which was attributed to the increase in viscosity ascribed to the GO (Figure 5d). Membranes 2021, 11, x FOR PEER REVIEW 10 of 25 3.1.3. Characterization of Prepared CTA and CTA/GO Membrane Contact Angle Prepared CTA and CTA/GO Membrane The contact angle values show that the CTA/GO membranes become more hydro- philic as GO- was incorporated into the cellulose triacetate membrane matrix. The water contact angle diminished from 65° (pure CTA membrane) to 47° as the amount of GO was increased to 0.3 wt-% GO. The water-loving membrane could drop off the immediate in- terplay between the adsorbed thin layer of water molecules on the top of the membrane [38]. The GO enhanced the membrane’s surface negativity due to the existence of oxygen- containing functional groups such as hydroxyl, epoxy groups, and carboxyl groups in GO which increase the interaction of membrane and water molecules, resulting in increased hydrophilicity. A significant decrease in contact angle after the addition of 0.3 wt-% GO content was observed, demonstrating a significant increase of surface hydrophilicity which is envis- aged to confer greater FO flux performance. This is supposed to be related to hydrophilic GO movement toward the top layer during phase inversion, leading to the lower water contact angles because of the GO’s superior attraction of OH groups, however, the contact angle of 0.5 wt-% GO was 54. This might be attributed to the bad dispersion of GO onto the surface of the membrane surface, as well as the bad compatibility and adhesive forces between the GO and the polymer, as the filler content was increased. SEM Prepared CTA and CTA/GO Membrane The morphological structures of the CTA and CTA-GO (0.1, 0.3, and 0.5 wt-%) mem- branes were evaluated through SEM (Figure 5). Pure CTA membranes showed the exist- ence of both sponge and a few macrovoid structures in the cross-section area, which is distinguishing of corresponding membranes [39,40]. The increase of these macrovoid Membranes 2022, 12, 6 10 of 24 structures on the addition of GO to CTA-GO membranes seems to be larger in comparison to pure CTA membranes (Figure 5). Membranes 2021, 11, x FOR PEER REVIEW 11 of 25 Figure 5. SEM images of the surface (magnification 800) and corresponding cross-section (magnifica- Figure 5. SEM images of the surface (magnification 800) and corresponding cross-section (magnification 2000) (a) Pure tion 2000) (a) Pure CTA, (b) 0.1 wt% wt% CA/GO, (c) 0.3 wt% wt% CA/GO, and (d) 0.5 wt% wt% CTA, (b) 0.1 wt-% wt-% CA/GO, (c) 0.3 wt-% wt-% CA/GO, and (d) 0.5 wt-% wt-% CA/GO. CA/GO. CTA-GO membranes are endowed with an appreciable pore size compared to that of pure CTA membranes, which give rise to high water permeability. The surface of the CA membrane, after the adding of GO, shows well distribution of GO particles onto the polymer matrix. Moreover, no cracks were observed on the membrane’s surface on the addition of GO indicating the GO membrane’s strength. From the SEM analysis, the cross-section area decreased in thickness after the addi- tion of 0.1 wt-% GO and could be due to hydrophilic GO particles, which can increase the rate of water (non-solvent) and solvent mixing during phase inversion, leading to a rela- tively lean top surface [41]. The thickness descends due to the incorporation of GO, which is aligned with previous studies [42]. Furthermore, an increase in the number of GO par- ticles augmented the viscosity of the dope solution leading to a diminished mass transfer rate of the non-solvent, giving rise to the thickness of the skin layer. When the quantity of GO on the CTA matrix was raised to 0.5 wt-%, macrovoids reduced and the connectivity of the holes was subdued, which was attributed to the increase in viscosity ascribed to the GO (Figure 5d). The Porosity of Prepared CTA/GO Membrane It is clear that the percentage porosity increased from 44 to 56% as the %GO increased to 0.5% compared with CTA membrane (Figure 6). As a result of the GO presence in the casting solution, the porosity of the CTA/GO membrane increased; extra pores developed on the membrane surface. OH and COOH of GO show the hydrophilic characteristics of polymer matrix and may improve the membrane synthesis process by boosting the rate of solvent/non-solvent exchange via the inversion technique [43]. The addition of GO in the casting solution increases hydrophilicity due to the strong attraction of water mole- cules by GO and the inclusion of hydrophilic OH and COOH groups on the active mem- brane substrate (AL). It is possible to deduce that the greater the porosity, the greater the permeability and the water flux. Membranes 2022, 12, 6 11 of 24 The Porosity of Prepared CTA/GO Membrane It is clear that the percentage porosity increased from 44 to 56% as the %GO increased to 0.5% compared with CTA membrane (Figure 6). As a result of the GO presence in the casting solution, the porosity of the CTA/GO membrane increased; extra pores developed on the membrane surface. OH and COOH of GO show the hydrophilic characteristics of polymer matrix and may improve the membrane synthesis process by boosting the rate of solvent/non-solvent exchange via the inversion technique [43]. The addition of GO in the casting solution increases hydrophilicity due to the strong attraction of water molecules by GO and the inclusion of hydrophilic OH and COOH groups on the active Membranes 2021, 11, x FOR PEER REVIEW 12 of 25 membrane substrate (AL). It is possible to deduce that the greater the porosity, the greater the permeability and the water flux. 0 0.1 0.3 0.5 % GO Figure 6. The % porosity as function of % GO incorporated in the prepared membrane. Figure 6. The % porosity as function of % GO incorporated in the prepared membrane. Mechanical Properties of Prepared CTA/GO Membrane Mechanical Properties of Prepared CTA/GO Membrane The mechanical assessment is one of the most important considerations for deter- The mechanical assessment is one of the most important considerations for determin- mining a component’s load-bearing capability. Mechanical properties are required for the ing a component’s load-bearing capability. Mechanical properties are required for the practical uses of a manufactured porous membrane. The vigor of the prepared CTA/GO practical uses of a manufactured porous membrane. The vigor of the prepared CTA/GO membranes was scanned and the findings represented in Figure 7a; the strength was membranes was scanned and the findings represented in Figure 7a; the strength was 18 18 MPa for the pure CTA membrane. By increasing the GO concentration, an increase in MPa for the pure CTA membrane. By increasing the GO concentration, an increase in the the membrane strength up to 35 MPa at 0.3 wt% GO loading was observed; further GO membrane strength up to 35 MPa at 0.3 wt-% GO loading was observed; further GO load- loading reduced the strength to 21.5 MPa. ing reduced the strength to 21.5 MPa. Figure 7b displays the Young’s modulus of the CTA/GO membrane, indicating a Figure 7b displays the Young’s modulus of the CTA/GO membrane, indicating a sim- similar behavior to the variations in strength. The existence of 0.3 wt% of GO resulted in an ilar behavior to the variations in strength. The existence of 0.3 wt-% of GO resulted in an optimal increase in Young’s modulus (0.95 GPa) compared to the CTA membrane (0.4 GPa). optimal increase in Young’s modulus (0.95 GPa) compared to the CTA membrane (0.4 The incorporation of GO enhanced the strength and Young’s membrane modulus for the GPa). The incorporation of GO enhanced the strength and Young’s membrane modulus fabricated CTA/GO membranes. The reinforcement effect was due to the efficient transition for the fabricated CTA/GO membranes. The reinforcement effect was due to the efficient of the mechanical characteristics of the graphene, which was also related to the highly transition of the mechanical characteristics of the graphene, which was also related to the interfacial adhesion between the GO and the CTA chains. Furthermore, GO’s wrinkled highly interfacial adhesion between the GO and the CTA chains. Furthermore, GO’s wrin- surface texture may induce mechanical overlapping and intensify adhesion to the polymer kled surface texture may induce mechanical overlapping and intensify adhesion to the matrix [44,45]. It was desirable to increase the performance of the graphene reinforcement polymer matrix [44,45]. It was desirable to increase the performance of the graphene rein- of the CTA membrane. At higher GO loads of more than 0.3 wt% percent, the strength, as forcement of the CTA membrane. At higher GO loads of more than 0.3 wt-% percent, the well as Young’s modulus, decreased. This could result from a reduction in the dispersion strength, as well as Young’s modulus, decreased. This could result from a reduction in the quality of GO in the matrix [45]. Therefore, the optimum strength and Young’s modulus dispersion quality of GO in the matrix [45]. Therefore, the optimum strength and Young’s were observed at 0.3 wt% GO, which was envisaged to fulfill the usage requirements. modulus were observed at 0.3 wt-% GO, which was envisaged to fulfill the usage require- ments. Porosity % Membranes 2022, 12, 6 12 of 24 Membranes 2021, 11, x FOR PEER REVIEW 13 of 25 1.2 30 b 0.8 20 0.6 0.4 0.2 0 0.2 0.4 0.6 0 0.2 0.4 0.6 GO Wt% GO Wt% Figure 7. (a) Membrane strength versus GO concentration and (b) and Young’s modulus for the CTA/GO membranes with Figure 7. (a) Membrane strength versus GO concentration and (b) and Young’s modulus for the increasing GO loading. CTA/GO membranes with increasing GO loading. The Parameters of Fabricated Membranes The Parameters of Fabricated Membranes The The pe permeation rmeation pr pro operties perties a and nd m membrane embrane p parameters arameters o of f f fabricated abricated m membranes embranes is is pr prese esented nted iin n Ta Table ble 2 2.. The The ex experimental perimental re results sults d demonstrated emonstrated tthat hat th the e CT CTA A/0.3 /0.3 wt wt% -% GO GO m membranes embranes pr pro ovided vided h higher igher wa water ter fflux lux a and nd co comparable mparable sa salt lt re rejection jection pe per rc centage entage d due ue t to o th the e a attained ttained sm small all B B/A /A ra ratio tio aand nd Js/J Js/Jw w raratio tio [4[6 46 –49] –49 . ]. Ta Table ble 2. 2. P Permeation ermeation pr pro operties perties of of fa fabricated bricated membranes. membranes. Js Js/Jw A B B/A Jw Js Js/Jw A B B/A GOwt% GOwt-% Jw (L/m .h) 2 2 2 1 1 2 1 2 −2 −1 −1 −2 −1 (L/m h) (g/m h) g/L (Lm h bar ) (Lm h ) (bar) (g/m .h) g/L (Lm h bar ) (Lm h ) (bar) 00 17 17 3.3 3.3 0.19 0.19 10.96 10.96 1.93 1.93 0.17 0.17 0.1 22 4.6 0.21 14.19 2.64 0.18 0.1 22 4.6 0.21 14.19 2.64 0.18 0.3 27 1.8 0.06 17.41 2,765 0.16 0.3 27 1.8 0.06 17.41 2,765 0.16 0.5 25 1.8 0.07 16.13 2.56 0.16 0.5 25 1.8 0.07 16.13 2.56 0.16 3.1.4. The Performance of Fabricated CTA/GO Membranes 3.1.4. The Performance of Fabricated CTA/GO Membranes The enhancement in hydrophilicity of the membranes was indicated by the decrease The enhancement in hydrophilicity of the membranes was indicated by the decrease in the water contact angle of the CTA/GO membranes from 65° (pure CTA membrane) to in the water contact angle of the CTA/GO membranes from 65 (pure CTA membrane) to 47°as GO content was increased to 0.3 wt-% GO. As a consequence, the water permeation 47 as GO content was increased to 0.3 wt% GO. As a consequence, the water permeation was improved. It was, however, observed that in the case of CTA/0.5 wt-% GO membrane, was improved. It was, however, observed that in the case of CTA/0.5 wt% GO membrane, the water flux of the membrane decreased, becoming even less than that of the pure CTA the water flux of the membrane decreased, becoming even less than that of the pure CTA membrane. This can be attributed to the use of graphene particles in the membrane matrix membrane. This can be attributed to the use of graphene particles in the membrane matrix as a hindrance to water flow. So, the average route was increased, which led to a reduction as a hindrance to water flow. So, the average route was increased, which led to a reduction in the permeate flow. In general, water flux was influenced by the hydrophilicity as well in the permeate flow. In general, water flux was influenced by the hydrophilicity as well as the hindrance effect of GO. Firstly, hydrophilicity may be the predominant force in as the hindrance effect of GO. Firstly, hydrophilicity may be the predominant force in comparatively low GO loads (up to 0.3 wt-%), then it was a hindrance to GO in higher comparatively low GO loads (up to 0.3 wt%), then it was a hindrance to GO in higher loads. loads. Secondly, the viscosity of the casting solution increased at with extra GO dose. It Secondly, the viscosity of the casting solution increased at with extra GO dose. It could could restrict the existence of large pores, which were easy to transport through water restrict the existence of large pores, which were easy to transport through water [50]. The [50]. The increased viscosity also contributed to a decline in the dispersion efficiency of increased viscosity also contributed to a decline in the dispersion efficiency of GO [46,47]. GO [46,47]. The reverse salt flux inversely proportioned to GO concentration Up to 0.3 percent wt. The reverse salt flux inversely proportioned to GO concentration Up to 0.3 percent When GO loading rose further, the reduction in reverse salt flow slowed down as a result of wt. When GO loading rose further, the reduction in reverse salt flow slowed down as a the hindrance effect of GO in the membrane. The J of the hybrid membranes was fairly low, result of the hindrance effect of GO in the membrane. The Js of the hybrid membranes was demonstrating a moderate salt rejection of the membranes [43,44]. The Js/Jw (specific salt fairly low, demonstrating a moderate salt rejection of the membranes [43,44]. The Js/Jw strenght (MPa) Young's Modulus (GPa) Membranes 2021, 11, x FOR PEER REVIEW 14 of 25 Membranes 2022, 12, 6 13 of 24 (specific salt flux) of CTA/0.3 wt-% GO was 0.06 g/L. Consequently, the CTA/0.3 wt-% GO membrane has good water permeation and low reverse salt flux compared to CTA mem- flux) of CTA/0.3 wt% GO was 0.06 g/L. Consequently, the CTA/0.3 wt% GO membrane brane. has good water permeation and low reverse salt flux compared to CTA membrane. The Effect of NaCl Concentration as a Draw Solution The Effect of NaCl Concentration as a Draw Solution Figure 8 shows the effect of different concentrations of NaCl as draw solutions (0.5 Figure 8 shows the effect of different concentrations of NaCl as draw solutions (0.5 and 2.5 M) with feed solutions of DI on the water flux as well as the RSF of neat CTA and 2.5 M) with feed solutions of DI on the water flux as well as the RSF of neat CTA and and CTA/GO membrane at a constant flow rate (1.55 L/min), temperature (25 C) and CTA/GO membrane at a constant flow rate (1.55 L/min), temperature (25 °C) and the ef- the effective membrane area of (56.3 2 cm ). Interestingly, it was detected that the water fective membrane area of (56.3 cm ). Interestingly, it was detected that the water fluxes 2 2 fluxes increased from 11 to 27 L/m 2 h whilst the RSF increased from 0.5 to 1.97 g/m 2h for increased from 11 to 27 L/m .h whilst the RSF increased from 0.5 to 1.97 g/m .h for CTA/0.3% GO. This might be attributed to increasing the osmotic driving force. This was CTA/0.3% GO. This might be attributed to increasing the osmotic driving force. This was owed to the enhancement of the net driving strength via the membrane for both water owed to the enhancement of the net driving strength via the membrane for both water and NaCl at a high DS content [51]. Comparing the RSF for CTA/0.3% GO membrane and NaCl at a high DS content [51]. Comparing the RSF for CTA/0.3% GO membrane with with the neat CTA membrane at different DS concentrations resulted in slightly higher the neat CTA membrane at different DS concentrations resulted in slightly higher RSF for RSF for CTA/0.3% GO membrane than the neat CTA membrane. This might be due to the CTA/0.3% GO membrane than the neat CTA membrane. This might be due to the salt salt concentration gradient growth over the membrane sides that provide a higher driving concentration gradient growth over the membrane sides that provide a higher driving force for the migration of NaCl ions from the DS side to the FS side [52]. force for the migration of NaCl ions from the DS side to the FS side [52]. 2.5 30 1.5 0.5 0 0 0.5 1 1.5 2 2.5 NaCl concentration Figure 8. The effect of NaCl concentration as a draw solution using CTA/0.3% GO under constant Figure 8. The effect of NaCl concentration as a draw solution using CTA/0.3% GO under constant operating conditions. operating conditions. Membrane Orientation and Its Impact on the Performance of the Fabricated Membranes Membrane Orientation and Its Impact on the Performance of the Fabricated Membranes TTwo wo modes modes can can be btested e tested by by facing facin the g th active e activ layer e layer either eith to erthe to th feed e fee solution d soluti (LA-FS) on (LA- FS) or the draw solution (AL-DS) utilizing DI and 2 M NaCl as FS and DS, respectively, or the draw solution (AL-DS) utilizing DI and 2 M NaCl as FS and DS, respectively, with awi 1.55 th a L/min 1.55 L/flow min frate. low ra The te. The CTA CT and A aCT nd A/0.3% CTA/0.3GO % GO membranes membranes flow flow rate rate atat AL-DS AL-DS orientation orientation wer were e slightly slightly higher higher with with respect respec to t to AL-FS AL-FS orientation orientatio (Figur n (Figure e 9a) 9a as)a ar s esult a resul of t the disappearance of internal concentration polarization (ICP) by utilizing the DI water as of the disappearance of internal concentration polarization (ICP) by utilizing the DI water FSs on the SL part of the prepared membrane [53,54]. as FSs on the SL part of the prepared membrane [53,54]. W Wa ater ter flowing flowing frfom rom the the feed feed tank tank via via the the membrane membrane SL SL dilutes dilutes DS DS at at the the membrane membrane surface, diminishing the osmotic pressure on the membrane surface and, as a result, limiting surface, diminishing the osmotic pressure on the membrane surface and, as a result, lim- the water flow [6]. iting the water flow [6]. Dilutive ICP has a significant impact on water flux in the FO process because the Dilutive ICP has a significant impact on water flux in the FO process because the osmotic pressure of the DS at the membrane boundary layer is critical to the FO process. osmotic pressure of the DS at the membrane boundary layer is critical to the FO process. Concentrative external concentration polarization (ECP) is missing on the AL side of the Concentrative external concentration polarization (ECP) is missing on the AL side of the membrane when DI is used as the FS in the FO style. membrane when DI is used as the FS in the FO style. The occurrence of the ICP is inverted when the system is set up in PRO mode. Because the PRO-style DS is facing the AL membrane, the effect is dilutive ECP, which can be Js (g/m2H) Jw (L/m2.H) Membranes 2021, 11, x FOR PEER REVIEW 15 of 25 Membranes 2022, 12, 6 14 of 24 The occurrence of the ICP is inverted when the system is set up in PRO mode. Be- cause the PRO-style DS is facing the AL membrane, the effect is dilutive ECP, which can reduced by delivering cross-flow shear to the membrane superficially. Because the concen- be reduced by delivering cross-flow shear to the membrane superficially. Because the con- trative ICP resides on the feed part of the membrane, its influence is less important than centrative ICP resides on the feed part of the membrane, its influence is less important that of the dilutive ICP, which explains why the water flow in the PRO mode is greater than that of the dilutive ICP, which explains why the water flow in the PRO mode is than that in the FO mode [11]. greater than that in the FO mode[11]. The RSF (Js) of CTA membrane were 1.5 and 3.3 g/m h in the AL-FS and AL-DS types, The RSF (Js) of CTA membrane were 1.5 and 3.3 g/m .h in the AL-FS and AL-DS respectively and for CTA/0.3 percent GO membrane were 0.8 and 1.8 g/m h in the FS-DS types, respectively and for CTA/0.3 percent GO membrane were 0.8 and 1.8 g/m .h in the direction and AL-DS direction sequentially (Figure 9a). The solute concentration of the FS-DS direction and AL-DS direction sequentially (Figure 9a). The solute concentration of membrane surface is higher in the PRO process mode than in the FO mode operation, the membrane surface is higher in the PRO process mode than in the FO mode operation, resulting in higher driving power and higher water flow. Higher draw concentration at resulting in higher driving power and higher water flow. Higher draw concentration at the membrane surface, on the other hand, typically resulted in higher RSF in the PRO the membrane surface, on the other hand, typically resulted in higher RSF in the PRO style style [48]. [48]. CTA 0.3% GO AL - DS AL-FS Mode of filtration (a) 3.5 2.5 CTA 1.5 0.3% GO 0.5 AL - DS AL-FS Mode of filtration (b) Figure 9. The effect of membrane orientation on (a) the water flux of and (b) on the reverse salt flux Figure 9. The effect of membrane orientation on (a) the water flux of and (b) on the reverse salt flux of CTA/0.3% GO compared with CTA membrane. of CTA/0.3% GO compared with CTA membrane. 2 2 Js (g/m .H) Jw (L/ m .H) M Membranes embranes 2 2022 021, , 11 12,, x 6 FOR PEER REVIEW 16 15 oof f 25 24 3.2. Formation of Polyamide Thin Film on CTA/0.3% GO Support 3.2. Formation of Polyamide Thin Film on CTA/0.3% GO Support TMC (Trimesoyl chloride) was used as a linking molecule to successfully synthesize TMC (Trimesoyl chloride) was used as a linking molecule to successfully synthesize polyamide (PA) on the cellulose triacetate (CTA) substrate. The PA coating on the CTA/0.3 polyamide (PA) on the cellulose triacetate (CTA) substrate. The PA coating on the CTA/0.3 percent GO membranes resulted in somewhat yellowish membranes. percent GO membranes resulted in somewhat yellowish membranes. SEM micrographs clearly display the traditional “ridge and valley” configuration of SEM micrographs clearly display the traditional “ridge and valley” configuration of PA (Figure 10b). However, there are clear distinctions between the neat CTA/0.3 percent PA (Figure 10b). However, there are clear distinctions between the neat CTA/0.3 percent GO displayed a smoother thick surface morphology (Figure 10a) with a few small pores GO displayed a smoother thick surface morphology (Figure 10a) with a few small pores structure and TFC membranes had rougher, grass-like structures. [24–26]. There were also structure and TFC membranes had rougher, grass-like structures. [24–26]. There were also more open top surface structures found. more open top surface structures found. Figure 10. SEM images (magnification 4000) of (a) CTA/0.3%GO substrates and (b) the PA- TFC membrane. Figure 10. SEM images (magnification 4000) of (a) CTA/0.3%GO substrates and (b) the PA-TFC The FI-IR spectra in Figure 11 indicate that distinctive CTA peaks were recorded at membrane. 1 1 1 1221 cm , 1369 cm , and 1720 cm , which were aligned with the expansion vibrations of C-O-C, C-CH , and C=O, respectively. Significant peaks at 3430 and 2939 cm were The FI-IR spectra in Figure 11 indicate that distinctive CTA peaks were recorded at correlated with the stretching vibration of the O-H and C-H bands, respectively, with −1 −1 −1 1221 cm , 1369 cm , and 1720 cm , which were aligned with the expansion vibrations of higher GO loading (0.3%) [55]. The presence of two significant peaks at 1661 cm and −1 C-O-C, C-CH3, and C=O, respectively. Significant peaks at 3430 and 2939 cm were corre- 1541 cm only occur on the top TFC surface membrane after IP reaction reflecting the lated with the stretching vibration of the O-H and C-H bands, respectively, with higher Membranes 2021, 11, x FOR PEER REVIEW 17 of 25 C=O expansion band (amide I) and C-N expansion band (amide II) of PA, consequently, −1 GO loading (0.3%) [55]. The presence of two significant peaks at 1661 cm-1 and 1541 cm confirms the effective development of PA thin film [56]. only occur on the top TFC surface membrane after IP reaction reflecting the C=O expan- sion band (amide I) and C-N expansion band (amide II) of PA, consequently, confirms the effective development of PA thin film [56]. Figure 11. ATR-FTIR spectra of (a) CTA/0.3% GO substrate and (b) the PA-TFC membrane. Figure 11. ATR-FTIR spectra of (a) CTA/0.3% GO substrate and (b) the PA-TFC membrane. 3.2.1. The Performance of Fabricated TFC Membranes TFC-FO membrane with CTA/0.3% GO substrates shows a high A value, revealing their superior water permeability and low salt permeability coefficient (B) [25] and lower (B/A) ratio (Table 3). Table 3. Permeation properties of fabricated membranes. Js/Jw B B/A 2 2 −2 −1 −1 GOwt-% Jw (L/m .h) Js (g/m h) A (Lm h bar ) R% −2 −1 g/L (Lm h ) (bar) CTA 17 3.3 0.19 10.96 1.93 0.17 85 CTA/0.3% GO 27 1.8 0.06 17.41 2,765 0.16 86 TFC 35 1.1 0.03 22.5 0.11 0.05 99.5 Figure 12 a indicates that the water flux Jw of TFC (CTA/0.3% GO) was 35 L/m .h in AL-DS mode, 30 L/m .h in AL-FS mode) are much higher than those of pure CTA (17 2 2 2 L/m .h in AL-DS mode, 15 L/m .h in AL-FS mode) and CTA/0.3% GO (27 L/m .h in AL- DS mode, 24.8 L/m .h in AL-FS mode) which indicates the enhancement of the water flux for prepared TFC membrane. Meanwhile, the reverse salt fluxes of the TFC (CTA/0.3% 2 2 GO) was 1.1 g/m .h in AL-DS mode, 0.9 g/m .h in AL-FS mode) are much lower than those 2 2 of pure CTA (3.3 g/m .h in AL-DS mode, 2.9 g/m .h in AL-FS mode) and CTA/0.3% GO 2 2 (1.8 g/m .h in AL-DS mode, 1.4 g/m .h in AL-FS mode) (Figure 12b). Therefore, the specific salt flux, Js/Jw of TFC (CTA/0.3% GO) substrate membrane was 0.03 g/L, telling that the TFC membrane held both good permeation for water as well as low reverse salt flux com- pared to CTA and CTA/0.3% GO membrane (Table 3). Membranes 2022, 12, 6 16 of 24 3.2.1. The Performance of Fabricated TFC Membranes TFC-FO membrane with CTA/0.3% GO substrates shows a high A value, revealing their superior water permeability and low salt permeability coefficient (B) [25] and lower (B/A) ratio (Table 3). Table 3. Permeation properties of fabricated membranes. Jw Js Js/Jw A (Lm B B/A GOwt% R% 2 2 1 1 2 1 (L/m h) (g/m h) g/L h bar ) (Lm h ) (bar) CTA 17 3.3 0.19 10.96 1.93 0.17 85 CTA/0.3% GO 27 1.8 0.06 17.41 2.765 0.16 86 TFC 35 1.1 0.03 22.5 0.11 0.05 99.5 Figure 12 a indicates that the water flux Jw of TFC (CTA/0.3% GO) was 35 L/m h in AL-DS mode, 30 L/m h in AL-FS mode) are much higher than those of pure CTA 2 2 2 (17 L/m h in AL-DS mode, 15 L/m h in AL-FS mode) and CTA/0.3% GO (27 L/m h in AL-DS mode, 24.8 L/m h in AL-FS mode) which indicates the enhancement of the water flux for prepared TFC membrane. Meanwhile, the reverse salt fluxes of the TFC (CTA/0.3% 2 2 GO) was 1.1 g/m h in AL-DS mode, 0.9 g/m h in AL-FS mode) are much lower than those 2 2 of pure CTA (3.3 g/m h in AL-DS mode, 2.9 g/m h in AL-FS mode) and CTA/0.3% GO 2 2 (1.8 g/m h in AL-DS mode, 1.4 g/m h in AL-FS mode) (Figure 12b). Therefore, the specific salt flux, Js/Jw of TFC (CTA/0.3% GO) substrate membrane was 0.03 g/L, telling that the TFC membrane held both good permeation for water as well as low reverse salt flux compared to CTA and CTA/0.3% GO membrane (Table 3). The enhancement in water flux of TFC with respect to CTA/GO membrane may be due to higher water sorption properties and swelling/deswelling effect of the PA layer. + + According to Donnan theory, there is an exchange of mobile ions (OH , Na , H or Cl ) between the macromolecule (PA layer) and the solution. This swelling/deswelling effect enhances the permeation properties of TFC as the result offast diffusion of water molecules across the membranes [57], as shown in Table 3 (a high A value, revealing their superior water permeability and low salt permeability coefficient (B) [58]. It is difficult to conduct a fair comparison between CA, CTA, and TFC-FO studies since they used different polymer weight percent, solvents, GO percent, and monomers for thin-film polymerizations and the type of DS used, however, Table 4 demonstrated the high performance of prepared CTA, CTA/GO, and TFC from palm frond, which was considered a challenge to prepare FO membrane from (CTA and GO) extracted from agriculture waste with superior performance than previously reported FO membranes prepared from commercial (CTA and GO). Membranes 2022, 12, 6 17 of 24 Membranes 2021, 11, x FOR PEER REVIEW 18 of 25 CTA 0.3% GO TFC AL - DS AL-FS Mode of filtration (a) 3.5 2.5 CTA 1.5 0.3% GO TFC 0.5 AL - DS AL-FS Mode of filtration (b) Figure 12. The effect of membrane orientation on (a) the water flux and (b) the reverse salt flux of Figure 12. The effect of membrane orientation on (a) the water flux and (b) the reverse salt flux of TFC (CTA/0.3% GO) substrate compared with CTA/0.3% GO and pure CTA membrane. TFC (CTA/0.3% GO) substrate compared with CTA/0.3% GO and pure CTA membrane. The enhancement in water flux of TFC with respect to CTA/GO membrane may be 3.2.2. FO Fabricated Membranes and Its Operation in Sea Water Sample due to higher water sorption properties and swelling/deswelling effect of the PA layer. The freshwater recovery from salty water is a favorable pressing issue confronting − + + − According to Donnan theory, there is an exchange of mobile ions (OH , Na , H or Cl ) Egypt at present, as the country suffers not only a water deficit but also a succession of between the macromolecule (PA layer) and the solution. This swelling/deswelling effect energy crises. The neat CTA/, CTA/0.3% GO, and polyamide TFC on CTA/0.3% GO enhances the permeation properties of TFC as the result offast diffusion of water mole- substrates were used for desalination of a natural seawater sample taken from Egypt’s cules across the membranes[57], as shown in Table 3 (a high A value, revealing their su- Hurghada-Red Sea coast utilizing NaCl as the DS. perior water permeability and low salt permeability coefficient (B) [58]. Tables 5–8 demonstrate the sample properties prior to the FO operation. The FS It is difficult to conduct a fair comparison between CA, CTA, and TFC-FO studies includes Red Sea collected water sample with 42,643 mg/L of total dissolved solid (TDS) since they used different polymer weight percent, solvents, GO percent, and monomers and 2 M NaCl as DS, a flow rate of 1.55 L/min at 25 C, and a membrane operation area of for thin-film polymerizations and the type of DS used, however, Table 4 demonstrated the 56.3 cm in FS-AL mode. high performance of prepared CTA, CTA/GO, and TFC from palm frond, which was con- The combination of high TDS and organics in the natural seawater sample resulted sidered a challenge to prepare FO membrane from (CTA and GO) extracted from agricul- in the effective concentration of constituents that was greater than that in the synthetic ture waste with superior performance than previously reported FO membranes prepared saltwater replica samples Figure 13. Furthermore, the natural seawater sample contains from commercial (CTA and GO). a large amount of strong TDS ions Tables 5–7. Membrane fouling, including organic Js (g/m2.H) Jw (L/ m2.H) Membranes 2022, 12, 6 18 of 24 foulants as well as inorganic foulants, is expected to be a significant cause of the intense flux decrease seen in Figure 13. As a result, as DS/FS concentrations shift, both external concentration polarization (ECP) and internal concentration polarization (ICP) change. High FS concentricity also led to an increase in ECP, which directly resulted in a significant reduction in the resulting water flux due to a decrease in osmotic pressure through the membranes [22]. (R%) of the FS is assessed by collecting and reviewing the DS sample at the end of each test (Table 8). After 3 h, all desalted permeated water samples were Membranes 2021, 11, x FOR PEER REVIEW 20 of 25 obtained for chemical analysis. Tables 9 and 10 reveal that TFC modified membranes have superior performance according to the quality of the produced permeate. 25 100 20 95 15 90 10 85 5 80 0 75 CTA CTA/0.3% GO TFC % R Jw Figure 13. Water flux and salt rejection using a natural seawater sample collected from Hurgada– Figure 13. Water flux and salt rejection using a natural seawater sample collected from Hurgada– Red Sea coast of Egypt and NaCl as the draw solution (DS) at 25 °C, flowrate1.55 L/min, FO mode: Red Sea coast of Egypt and NaCl as the draw solution (DS) at 25 C, flowrate1.55 L/min, FO with cells vertically oriented, and active layer—faced feed solution (AL-FS), using Neat CTA, mode: with cells vertically oriented, and active layer—faced feed solution (AL-FS), using Neat CTA, CTA/0.3%GO, and TFC modified membranes. CTA/0.3%GO, and TFC modified membranes. Table 5. Physico-chemical analysis of seawater. Table 4. Comparison between FO prepared membranes in the present work and previously reported FO membranes. Parameters Unit Results pH - 8.1 Polymer Weight % GO Weight % FluxL/m h DS Citation Sand content N.D CA/GO 0.15 16 4 M glucose [59] Total solids mg/L 42,702 CTA 15.2 2 M glucose [22] Total dissolved solids mg/L 42,643 Suspended solids mg/L 59 CTA/GO 0.6% 18.43 0.5 M NaCl [22] Total hardness (CaCO3) mg/L 7200 GO/Acetic 0.4% 33.5 1 M NH Cl [11] Acid/CTA/CA Calcium hardness (CaCO3) mg/L 1040 Magnesium hardness (CaCO3) mg/L 6160 CTA/Zn2Cl/Lactic acid - 11.5 2 M glucose [26] Total alkalinity mg/L 104 CTA Prepared From Present - 17 2 M NaCl Bicarbonate mg/L 80 Palm Fronds work Carbonate mg/L 12 CTA/GO Prepared 0.3% prepared Present 27 2 M NaCl Hydroxide mg/L 0 From Palm Fronds from palm fronds work Methyl Orange alkalinity mg/L 92 0.3% Present Phenolphthalein alkalinity mg/L 12 TFC/CTA prepared from 35 2 M NaCl work palm fronds Acidity mg/L 12 Sulfate mg/L 2200 Chloride (Cl ) mg/L 25,000 Nitrite (𝑁𝑂 -N) mg/L <0.005 Nitrate (𝑁𝑂 -N) mg/L <0.05 Ammonium nitrogen mgN/L <0.01 Free carbon dioxide mg/L 0.1 Phosphorus mg/L <0.01 Total silica mg/L <0.01 Non-reactive silica mg/L <0.01 Sodium (Na) mg/L 19200 Potassium (K) mg/L 940 Calcium (Ca) mg/L 416 Magnesium (Mg) mg/L 1498 Jw (L/m2.H) %R Membranes 2022, 12, 6 19 of 24 Table 5. Physico-chemical analysis of seawater. Parameters Unit Results pH - 8.1 Sand content N.D Total solids mg/L 42,702 Total dissolved solids mg/L 42,643 Suspended solids mg/L 59 Total hardness (CaCO ) mg/L 7200 Calcium hardness (CaCO ) mg/L 1040 Magnesium hardness mg/L 6160 (CaCO ) Total alkalinity mg/L 104 Bicarbonate mg/L 80 Carbonate mg/L 12 Hydroxide mg/L 0 Methyl Orange alkalinity mg/L 92 Phenolphthalein alkalinity mg/L 12 Acidity mg/L 12 Sulfate mg/L 2200 Chloride (Cl ) mg/L 25,000 Nitrite (NO -N) mg/L <0.005 Nitrate (NO -N) mg/L <0.05 Ammonium nitrogen mgN/L <0.01 Free carbon dioxide mg/L 0.1 Phosphorus mg/L <0.01 Total silica mg/L <0.01 Non-reactive silica mg/L <0.01 Sodium (Na) mg/L 19,200 Potassium (K) mg/L 940 Calcium (Ca) mg/L 416 Magnesium (Mg) mg/L 1498 Table 6. Organic analysis of seawater. Parameters Unit Results Chemical Oxygen Demand mgO /L 14 Biological Oxygen Demand mgO /L 1.5 Oil & grease mg/L 4.5 Total Organic Carbon mgC/L 3.5 Table 7. Biological and microbiological examination of sea water. Parameters Unit Results Total bacterial count (22 C) Count/mL 2 Total bacterial count (37 C) Count/mL 1 Total Coliform MPN-index/100 mL N.D Fecal Coliform MPN-index/100 mL N.D Fecal Streptococci MPN-index/100 mL N.D Blue Green Algae Org/mL N.D Total Algal Count Org/mL 40 Membranes 2022, 12, 6 20 of 24 Table 8. Characteristics of real saline water sample prior and post FO desalination of Neat CTA, CTA/0.3%GO, and TFC modified membranes and NaCl as the DS. Concentrations Ions (mg/L) of Sea Water R%of Effluent after FO System. before FO System. TFC Modified Neat CTA CTA/0.3%GO Membranes Total Dissolved 42,643 83 84.2 98.5 Solids Calcium (Ca) 416 83 84 98 Magnesium 1498 83 84.2 98.8 (Mg) Sodium (Na) 19,200 90 93 99 Potassium (K) 940 84 84.3 99 Carbonate 12 83 84.2 99 Sulfate 2200 83 84.4 98 Chloride (Cl ) 25,000 83.3 85 99 It is revealed that, for the FO process, TFC on CTA/0.3% GO substrate membrane led to better salt rejection than neat CTA and CTA/0.3% GO membranes. FO technique has many advantages, such as decreasing the amount of salt without using hydraulic pressure and it is considered an ecologically friendly technique where it not only saves energy but also it saves desalination cost. Tables 9 and 10 compare the permeate water quality of TFC on CTA/0.3% GO against the Egyptian Ministerial decree No. 458/2007 for drinking water. The water showed that the permeate water meets the guidelines for drinking water. Table 9. Physico-chemical analysis for seawater and permeate. The Egyptian Parameters Unit Feed Permeate Ministerial Decree No. 458/2007 pH - 8.1 7.5 6.5–8.5 Total Dissolved Solids mg/L 42,643 640 1000 Suspended Solids mg/L 59 3 - Total Hardness mg/L 7200 110 500 (CaCO ) Calcium Hardness mg/L 1040 21 350 (CaCO ) Magnesium Hardness mg/L 6160 99 150 (CaCO ) Total Alkalinity mg/L 104 92 - Bicarbonate mg/L 92 92 - Carbonate mg/L 12 0 - Hydroxide mg/L 0 0 - Sulfate mg/L 2200 40 250 Chloride (Cl ) mg/L 25,000 250 250 Nitrite (NO -N) mg/L <0.005 <0.005 0.2 Nitrate (NO -N) mg/L <0.05 45 Ammonium Nitrogen mgN/L <0.01 <0.01 - Free Carbon Dioxide mg/L 0.1 N.D - Phosphorus mg/L <0.01 <0.01 - Total Silica mg/L <0.01 <0.01 - Non reactive Silica mg/L <0.01 <0.01 - Sodium (Na) mg/L 19,200 186 200 Potassium (K) mg/L 940 7 - Calcium (Ca) mg/L 416 9 - Magnesium (Mg) mg/L 1498 18 - Membranes 2022, 12, 6 21 of 24 Table 10. Organic analysis for seawater and permeate. The Egyptian Parameters Unit Feed Permeate Ministerial Decree No. 458/2007 Chemical Oxygen mgO /L 14 2 - Demand Biological Oxygen mgO /L 1.5 N.D - Demand Oil & grease/’ mg/L 4.5 0.12 - Total Organic Carbon mgC/L 3.5 0.4 - 4. Conclusions CTA/GO membranes were synthesized by phase inversion using CTA and GO pre- pared from palm fronds. The GO% ranged from 0.1–0.5%. The GO incorporation into the CTA matrix led to an increase the membrane hydrophilicity, porosity, and mechanical strength. These increases resulted in significant improvement in water flux as compared to neat CTA. The water contact angle diminished from 65 (pure CTA membrane) to 47 as the amount of GO was increased to 0.3 wt% GO% porosity increased from 44 to 56% as the content of GO increased to 0.5 wt% compared with that of CTA membrane. The enhancement in the hydrophilicity and mechanical strength of the membrane due to the high attraction of water molecules by GO and the inclusion of hydrophilic reactive groups (OH and COOH) on the active membrane substrate (AL). The specific salt flux, Js/Jw, of the TFC (CTA/0.3% GO) substrate membrane was 0.03 g/L which is lower than CTA and CTA/GO. As a result, the TFC membrane surpassed the CTA and CTA/0.3 percent GO membranes in terms of both water permeability and reverse salt flux. A real salty water sample from Egypt’s Red Sea coast was used as the feed, with the draw solution of NaCl at 25 C and flow rate1.55 L/min. The quality of desalted permeate indicated that the high-performance polyamide TFC–CTA/0.3% GO. As a result, the prepared TFC–CTA showed a high potential for interest in saline water desalination. Consequently, the TFC membrane platform will most likely replace the CA membrane for FO, particularly when combined with a renewable energy DS recovery system, where such energies would only be used for solute recovery. Author Contributions: Conceptualization, T.S.J. and R.M.; methodology, R.A.N., H.A.A., T.I.M.R. and S.X.; validation, R.M.; formal analysis, R.A.N., H.A.A., T.I.M.R. and R.M.; investigation, T.S.J., R.M.; resources, T.S.J. and R.M.; data curation, T.S.J., R.A.N., H.A.A. and S.X.; writing—original draft preparation, T.S.J., R.A.N., H.A.A. and T.I.M.R.; writing—review and editing, T.S.J., R.A.N., H.A.A. and R.M.; visualization, T.S.J., R.A.N. and H.A.A.; supervision, T.S.J. and R.M.; project administration, T.S.J., and R.M.; funding acquisition, T.S.J. and R.M. All authors have read and agreed to the published version of the manuscript. Funding: Science, Technology and Innovation Funding Authority in Egypt and the National Research Foundation (South Africa) for financing the work through collaborative project number [27873] in Egypt. Institutional Review Board Statement: Not applicable. Informed Consent Statement: Not applicable. Data Availability Statement: No applicable. Acknowledgments: The authors would like to acknowledge the Science, Technology and Innovation Funding Authority in Egypt and the National Research Foundation (South Africa) for financing the work through collaborative project number [27873] in Egypt. Conflicts of Interest: The authors declare no conflict of interest. Membranes 2022, 12, 6 22 of 24 References 1. Sidney, L.; Srinivasa, S. High Flow Porous Membranes for Separating Water from Saline Solutions. U.S. Patent 3,133,132, 12 May 1964. 2. Loeb, S.; Van Hessen, F.; Levi, J.; Ventura, M. The osmotic power plant. In Proceedings of the 11th Intersociety Energy Conversion Engineering Conference, State Line, Nevada, 12–17 September 1976; Volume 1, pp. 51–57. 3. Shaffer, D.L.; Werber, J.R.; Jaramillo, H.; Lin, S.; Elimelech, M. Forward osmosis: Where are we now? Desalination 2015, 356, 271–284. [CrossRef] 4. Jiao, Y.; Kang, Y.; Yang, C. Osmosis and Its Applications. Encycl. Microfluid. Nanofluidics 2015, 2622–2633. [CrossRef] 5. Ali, A.; Tufa, R.A.; Macedonio, F.; Curcio, E.; Drioli, E. Membrane technology in renewable-energy-driven desalination. Renew. Sustain. Energy Rev. 2018, 81, 1–21. [CrossRef] 6. Chen, G.; Wang, Z.; Nghiem, L.; Li, X.-M.; Xie, M.; Zhao, B.; Zhang, M.; Song, J.; He, T. Treatment of shale gas drilling flowback fluids (SGDFs) by forward osmosis: Membrane fouling and mitigation. Desalination 2015, 366, 113–120. [CrossRef] 7. Li, X.; He, T.; Dou, P.; Zhao, S. 2.5 Forward Osmosis and Forward Osmosis Membranes. Chem. Mol. Sci. Chem. Eng. 2017, 2, 95–123. [CrossRef] 8. Wang, K.Y.; Ong, R.C.; Chung, T.-S. Double-Skinned Forward Osmosis Membranes for Reducing Internal Concentration Polarization within the Porous Sublayer. Ind. Eng. Chem. Res. 2010, 49, 4824–4831. [CrossRef] 9. Su, J.; Chung, T.-S.; Helmer, B.J.; de Wit, J.S. Enhanced double-skinned FO membranes with inner dense layer for wastewater treatment and macromolecule recycle using Sucrose as draw solute. J. Memb. Sci. 2012, 396, 92–100. [CrossRef] 10. Zhang, S.; Wang, K.Y.; Chung, T.-S.; Jean, Y.; Chen, H. Molecular design of the cellulose ester-based forward osmosis membranes for desalination. Chem. Eng. Sci. 2011, 66, 2008–2018. [CrossRef] 11. Ahmed, D.F.; Isawi, H.; Badway, N.A.; Elbayaa, A.; Shawky, H. Graphene oxide incorporated cellulose triacetate/cellulose acetate nanocomposite membranes for forward osmosis desalination. Arab. J. Chem. 2021, 14, 102995. [CrossRef] 12. Liang, J.; Huang, Y.; Zhang, F.; Zhang, Y.; Li, N.; Chen, Y. The use of graphene oxide membranes for the softening of hard water. Sci. China Ser. E Technol. Sci. 2014, 57, 284–287. [CrossRef] 13. Qin, D.; Liu, Z.; Bai, H.; Sun, D.D. Three-dimensional architecture constructed from a graphene oxide nanosheet–polymer composite for high-flux forward osmosis membranes. J. Mater. Chem. A 2017, 5, 12183–12192. [CrossRef] 14. Lu, P.; Liang, S.; Zhou, T.; Mei, X.; Zhang, Y.; Zhang, C.; Umar, A.; Wang, H.; Wang, Q. Typical Thin-Film Composite (TFC) Membranes Modified with Inorganic Nanomaterials for Forward Osmosis: A Review. Nanosci. Nanotechnol. Lett. 2016, 8, 906–916. [CrossRef] 15. Zhang, S.; Wang, K.Y.; Chung, N.T.-S.; Chen, H.; Jean, Y.; Amy, G. Well-constructed cellulose acetate membranes for forward osmosis: Minimized internal concentration polarization with an ultra-thin selective layer. J. Membr. Sci. 2010, 360, 522–535. [CrossRef] 16. Yip, N.Y.; Tiraferri, A.; Phillip, W.A.; Schiffman, J.D.; Elimelech, M. High performance thin-film composite forward osmosis membrane. Environ. Sci. Technol. 2010, 44, 3812–3818. [CrossRef] 17. Wang, R.; Shi, L.; Tang, C.Y.; Chou, S.; Qiu, C.; Fane, A.G. Characterization of novel forward osmosis hollow fiber membranes. J. Membr. Sci. 2010, 355, 158–167. [CrossRef] 18. Ragab, T.I.; Amer, H.; Wasfy, A.A.F.; Hady, M.A.; Mossa, A.T.H.; Liebner, F. Sulfated Cellulose from Agriculture Wastes, Anticoagulant, Fibrinolytic and Toxicological Studies. J. Environ. Sci. Technol. 2014, 7, 266–280. [CrossRef] 19. Ragab, T.I.; Wasfy, A.A.; Amer, H.; El-Gendi, A.; Abdel-Hady, M.; Liebner, F. Synthesis of Cellulose Acetate Membrane from the Egyptian Rice Straws. J. Appl. Sci. 2014, 14, 3424–3435. [CrossRef] 20. Hummers, W.S., Jr.; Offeman, R.E. Preparation of graphitic oxide. J. Am. Chem. Soc. 1958, 80, 1339. [CrossRef] 21. Qiu, C.; Qi, S.; Tang, C.Y. Synthesis of high flux forward osmosis membranes by chemically crosslinked layer-by-layer polyelec- trolytes. J. Membr. Sci. 2011, 381, 74–80. [CrossRef] 22. Li, G.; Li, X.-M.; He, T.; Jiang, B.; Gao, C. Cellulose triacetate forward osmosis membranes: Preparation and characterization. Desalination Water Treat. 2013, 51, 2656–2665. [CrossRef] 23. Baker, R.W. Membrane Technology and Applications; John Wiley & Sons: Hoboken, NJ, USA, 2012; ISBN 1118359690. 24. Alsvik, I.L.; Nilsen, T.-N.; Haegg, M.-B. Thin Film Composite Polyamide Membranes on a Hydrophilic Cellulose Acetate Support for Pressure Retarded Osmosis. In Proceedings of the Renewable Energy Research Conference 2010, Trondheim, Norway, 6 July–6 August 2010. 25. Zheng, K.; Zhou, S.; Zhou, X. A low-cost and high-performance thin-film composite forward osmosis membrane based on an SPSU/PVC substrate. Sci. Rep. 2018, 8, 1–13. [CrossRef] 26. Chen, X.; Xu, J.; Lu, J.; Shan, B.; Gao, C. Enhanced performance of cellulose triacetate membranes using binary mixed additives for forward osmosis desalination. Desalination 2017, 405, 68–75. [CrossRef] 27. Freire, C.S.R.; Silvestre, A.J.D.; Neto, C.P.; Belgacem, M.N.; Gandini, A. Controlled heterogeneous modification of cellulose fibers with fatty acids: Effect of reaction conditions on the extent of esterification and fiber properties. J. Appl. Polym. Sci. 2006, 100, 1093–1102. [CrossRef] 28. Maneerung, T.; Tokura, S.; Rujiravanit, R. Impregnation of silver nanoparticles into bacterial cellulose for antimicrobial wound dressing. Carbohydr. Polym. 2008, 72, 43–51. [CrossRef] 29. Liu, D.; Zhong, T.; Chang, P.R.; Li, K.; Wu, Q. Starch composites reinforced by bamboo cellulosic crystals. Bioresour. Technol. 2010, 101, 2529–2536. [CrossRef] Membranes 2022, 12, 6 23 of 24 30. French, A.D. Idealized powder diffraction patterns for cellulose polymorphs. Cellulose 2013, 21, 885–896. [CrossRef] 31. Hu, W.; Chen, S.; Xu, Q.; Wang, H. Solvent-free acetylation of bacterial cellulose under moderate conditions. Carbohydr. Polym. 2011, 83, 1575–1581. [CrossRef] 32. Saikia, C.; Ali, F.; Goswami, T.; Ghosh, A.C. Esterification of high -cellulose extracted from Hibiscus cannabinus L. Ind. Crops Prod. 1995, 4, 233–239. [CrossRef] 33. Sun, X.F.; Sun, R.C.; Sun, J.X. Acetylation of sugarcane bagasse using NBS as a catalyst under mild reaction conditions for the production of oil sorption-active materials. Bioresour. Technol. 2004, 95, 343–350. [CrossRef] 34. Luz, S.M.; Del Tio, J.; Rocha, G.J.M.; Gonçalves, A.R.; Del’Arco, A.P., Jr. Cellulose and cellulignin from sugarcane bagasse reinforced polypropylene composites: Effect of acetylation on mechanical and thermal properties. Compos. Part A Appl. Sci. Manuf. 2008, 39, 1362–1369. [CrossRef] 35. Shahriary, L.; Athawale, A.A. Graphene oxide synthesized by using modified hummers approach. Int. J. Renew. Energy Environ. Eng. 2014, 2, 58–63. 36. Somanathan, T.; Prasad, K.; Ostrikov, K.; Saravanan, A.; Krishna, V.M. Graphene Oxide Synthesis from Agro Waste. Nanomaterials 2015, 5, 826–834. [CrossRef] 37. Du, Q.; Zheng, M.; Zhang, L.; Wang, Y.; Chen, J.; Xue, L.; Dai, W.; Ji, G.; Cao, J. Preparation of functionalized graphene sheets by a low-temperature thermal exfoliation approach and their electrochemical supercapacitive behaviors. Electrochim. Acta 2010, 55, 3897–3903. [CrossRef] 38. Tiraferri, A.; Kang, Y.; Giannelis, E.P.; Elimelech, M. Superhydrophilic Thin-Film Composite Forward Osmosis Membranes for Organic Fouling Control: Fouling Behavior and Antifouling Mechanisms. Environ. Sci. Technol. 2012, 46, 11135–11144. [CrossRef] [PubMed] 39. Zhu, J.; Tian, M.; Hou, J.; Wang, J.; Lin, J.; Zhang, Y.; Liu, J.; Van der Bruggen, B. Surface zwitterionic functionalized graphene oxide for a novel loose nanofiltration membrane. J. Mater. Chem. A 2015, 4, 1980–1990. [CrossRef] 40. Zinadini, S.; Zinatizadeh, A.A.; Rahimi, M.; Vatanpour, V.; Zangeneh, H. Preparation of a novel antifouling mixed matrix PES membrane by embedding graphene oxide nanoplates. J. Membr. Sci. 2014, 453, 292–301. [CrossRef] 41. Ghaemi, N.; Madaeni, S.S.; Alizadeh, A.; Rajabi, H.; Daraei, P. Preparation, characterization and performance of polyethersul- fone/organically modified montmorillonite nanocomposite membranes in removal of pesticides. J. Membr. Sci. 2011, 382, 135–147. [CrossRef] 42. Zhu, J.; Tian, M.; Zhang, Y.; Zhang, H.; Liu, J. Fabrication of a novel “loose” nanofiltration membrane by facile blending with Chitosan–Montmorillonite nanosheets for dyes purification. Chem. Eng. J. 2015, 265, 184–193. [CrossRef] 43. Mansourpanah, Y.; Madaeni, S.; Rahimpour, A.; Adeli, M.; Hashemi, M.; Moradian, M. Fabrication new PES-based mixed matrix nanocomposite membranes using polycaprolactone modified carbon nanotubes as the additive: Property changes and morphological studies. Desalination 2011, 277, 171–177. [CrossRef] 44. Wang, X.; Song, M. Toughening of polymers by graphene. Nanomater. Energy 2013, 2, 265–278. [CrossRef] 45. Rafiee, M.A.; Rafiee, J.; Srivastava, I.; Wang, Z.; Song, H.; Yu, Z.-Z.; Koratkar, N. Fracture and Fatigue in Graphene Nanocomposites. Small 2010, 6, 179–183. [CrossRef] 46. Khorshidi, B.; Thundat, T.; Fleck, B.; Sadrzadeh, M. A Novel Approach toward Fabrication of High Performance Thin Film Composite Polyamide Membranes. Sci. Rep. 2016, 6, 22069. [CrossRef] 47. Xiaoxiao, S.; Ja, P. Relating Water/Solute Permeability Coefficients to the Performance of Thin-Film Nanofiber Composite Forward Osmosis Membrane. J. Membr. Sci. Technol. 2016, 6, 1–10. [CrossRef] 48. Wang, Y.; Fang, Z.; Zhao, S.; Ng, D.; Zhang, J.; Xie, Z. Dopamine incorporating forward osmosis membranes with enhanced selectivity and antifouling properties. RSC Adv. 2018, 8, 22469–22481. [CrossRef] 49. Guan, Y.-F.; Huang, B.-C.; Wang, Y.-J.; Gong, B.; Lu, X.; Yu, H.-Q. Modification of forward osmosis membrane with naturally- availablehumic acid: Towards simultaneously improved filtration performance and antifouling properties. Environ. Int. 2019, 131, 105045. [CrossRef] [PubMed] 50. Lee, J.; Chae, H.-R.; Won, Y.J.; Lee, K.; Lee, C.-H.; Lee, H.H.; Kim, I.-C.; Lee, J.-M. Graphene oxide nanoplatelets composite membrane with hydrophilic and antifouling properties for wastewater treatment. J. Membr. Sci. 2013, 448, 223–230. [CrossRef] 51. Li, C.; Song, J.; Dou, P.; Yin, Y.; He, T.; He, W. Effects of low-toxicity solvent and binary mixed additives on the microstructure and performance of cellulose triacetate (CTA) membranes for forward osmosis. Desalination Water Treat. 2018, 130, 44–53. [CrossRef] 52. Sahebi, S.; Sheikhi, M.; Ramavandi, B.; Ahmadi, M.; Zhao, S.; Adeleye, A.S.; Shabani, Z.; Mohammadi, T. Sustainable management of saline oily wastewater via forward osmosis using aquaporin membrane. Process. Saf. Environ. Prot. 2020, 138, 199–207. [CrossRef] 53. Akther, N.; Yuan, Z.; Chen, Y.; Lim, S.; Phuntsho, S.; Ghaffour, N.; Matsuyama, H.; Shon, H. Influence of graphene oxide lateral size on the properties and performances of forward osmosis membrane. Desalination 2020, 484, 114421. [CrossRef] 54. Phuntsho, S.; Sahebi, S.; Majeed, T.; Lotfi, F.; Kim, J.E.; Shon, H.K. Assessing the major factors affecting the performances of forward osmosis and its implications on the desalination process. Chem. Eng. J. 2013, 231, 484–496. [CrossRef] 55. Li, F.; Sun, M.; Cheng, Q.; Yang, B. Preparation and Characterization of Graphene Oxide/Cellulose Triacetate Forward Osmosis Membranes. In Proceedings of the International Symposium on Materials Application and Engineering (SAME 2016), Chiang Mai, Thailand, 20–21 August 2016; Volume 67, p. 1015. Membranes 2022, 12, 6 24 of 24 56. Wu, Q.-Y.; Xing, X.-Y.; Yu, Y.; Gu, L.; Xu, Z.-K. Novel thin film composite membranes supported by cellulose triacetate porous substrates for high-performance forward osmosis. Polymer 2018, 153, 150–160. [CrossRef] 57. Alsvik, I.L.; Zodrow, K.; Elimelech, M.; Hägg, M.-B. Polyamide formation on a cellulose triacetate support for osmotic membranes: Effect of linking molecules on membrane performance. Desalination 2013, 312, 2–9. [CrossRef] 58. Ren, J.; McCutcheon, J.R. A new commercial thin film composite membrane for forward osmosis. Desalination 2014, 343, 187–193. [CrossRef] 59. Wang, X.; Liu, S.Q.; Hou, S.F.; Lu, P.; Hou, K.; Wang, Z.P.; Wang, L.G. Preparation and characterization of CA/GO mixed matrix forward osmosis membranes. In Proceedings of the International Symposium on Mechanical Engineering and Material Science (Ismems-16), Jeju Island, Korea, 17–19 November 2016; Atlantis Press: Paris, France, 2016.
http://www.deepdyve.com/assets/images/DeepDyve-Logo-lg.png
Membranes
Multidisciplinary Digital Publishing Institute
http://www.deepdyve.com/lp/multidisciplinary-digital-publishing-institute/low-cost-high-performance-polyamide-thin-film-composite-cellulose-0BmwGgzylC