AbstractA series of single-hole hollow polyester fiber (SHHPF) reinforced hydrogenated carboxyl nitrile rubber (HXNBR) composites were fabricated. In this study, the sound absorption property of the HXNBR/SHHPF composite was tested in an impedance tube, the composite morphology was characterized by scanning electron microscope (SEM), and the tensile mechanical property was measured by strength tester. The results demonstrated that a remarkable change in sound absorption can be observed by increasing the SHHPF content from 0% to 40%. In the composite with 40% SHHPF in 1 mm thickness, the sound absorption coefficient reached 0.671 at 2,500 Hz; the effective bandwidth was 1,800-2,500 Hz for sound absorption coefficient larger than 0.2. But the sound absorption property of the composite deteriorated when the SHHPF content increased to 50% in 1 mm thickness. While with 20% SHHPF proportion, the sound absorption property was improved by increasing the thickness of composites from 1 to 5 mm. Compared with the pure HXNBR of the same thickness, the tensile mechanical property of the composite improved significantly by increasing the SHHPF proportion. As a lightweight composite with excellent sound absorption property, the HXNBR/SHHPF composite has potential practical application value in the fields of engineering.
Autex Research Journal – de Gruyter
Published: Sep 26, 2017