B. Belkessa, D. Miroud, Naima Ouali, B. Cheniti (2016)
Microstructure and Mechanical Behavior in Dissimilar SAF 2205/API X52 Welded PipesActa Metallurgica Sinica (English Letters), 29
W. Faes, S. Lecompte, Z. Ahmed, J. Bael, R. Salenbien, K. Verbeken, M. Paepe (2019)
Corrosion and corrosion prevention in heat exchangersCorrosion Reviews, 37
AbstractThis paper is focused on the problematics of weld joint corrosive degradation in the boiler water environment. The boiler water is commonly used in power industry. The corrosion experiment simulated the boiler water environment during shutdown, when chemicals may be concentrated in the deposits, or as a result of evaporation. The corrosion experiment was performed on heterogeneous weldments made of P265GH//X6CrNiTi18-9 steels in the environment of stagnant boiler water with the addition of NaCl for 53 days. The data showed only minimal weight losses, and small changes in the measured fracture toughness of the welded joint. At the same time, a tendency for a mechanical weakening of the welded joint with the increasing aggressivity of the boiler water environment was observed. The metallographic analysis was performed to describe the nature of corrosive degradation.
Koroze a ochrana materialu – de Gruyter
Published: Jan 1, 2022
Read and print from thousands of top scholarly journals.
Already have an account? Log in
Bookmark this article. You can see your Bookmarks on your DeepDyve Library.
To save an article, log in first, or sign up for a DeepDyve account if you don’t already have one.
Copy and paste the desired citation format or use the link below to download a file formatted for EndNote
Access the full text.
Sign up today, get DeepDyve free for 14 days.
All DeepDyve websites use cookies to improve your online experience. They were placed on your computer when you launched this website. You can change your cookie settings through your browser.